中外常用钢号对照表及化学成分
作者:
来源:
发布时间:2009/11/13 14:11:52 点击数:5368
产品名 称标准 |
牌号 |
化学成分% |
国外产品牌号 |
C |
Si |
Mn |
Cr |
Ni |
Mo |
Cu |
Ti |
S |
P |
Al |
美国 |
日本 |
德国 |
不锈钢 GB1220-92 |
00Cr19Ni10 |
≤0.03 |
≤1.0 |
≤2.0 |
18.0~20.0 |
8.0~12.0 |
- |
- |
- |
≤0.03 |
≤0.035 |
- |
304L |
SUS304L |
X2CrNi -18.9 |
1Cr19Ni12 |
≤0.12 |
≤1.0 |
≤2.0 |
17.0~19.0 |
10.5~13.0 |
- |
- |
- |
≤0.03 |
≤0.035 |
- |
305 |
SUS305 |
X5CrNi -19.11 |
0Cr25Ni12 |
≤0.08 |
≤1.0 |
≤2.0 |
24.0~26.0 |
19.0~22.0 |
- |
- |
- |
≤0.03 |
≤0.035 |
- |
310S |
SUS-310S |
|
0Cr17Ni12Mo2 |
≤0.08 |
≤1.0 |
≤2.0 |
16.0~18.5 |
10.0~14.0 |
2.0~3.0 |
- |
- |
≤0.03 |
≤0.035 |
- |
316 |
SUS316 |
X5CrNi -Mo18.1 |
00Cr17Ni14Mo2 |
≤0.03 |
≤1.0 |
≤2.0 |
16.0~18.0 |
12.0~15.0 |
2.0~3.0 |
- |
- |
≤0.035 |
≤0.035 |
- |
316L |
SUS316L |
X2CrN i-Mo18.1 |
1Cr18Ni12Mo2Ti |
≤0.12 |
≤1.0 |
≤2.0 |
16.0~19.0 |
11.0~14.0 |
1.8~2.5 |
- |
5*(c%-0.02~0.8 |
≤0.03 |
≤0.035 |
- |
|
|
X10CrNi -MoTi |
0Cr18Ni12Mo2Ti |
≤0.08 |
≤1.0 |
≤2.0 |
16.0~19.0 |
11.0~14.0 |
1.8~25 |
- |
5*c%~0.7 |
≤0.03 |
≤0.035 |
- |
316Ti |
SUS316Ti |
X10CrNi- MoTi18.0 |
1Cr18Ni9Ti |
≤0.12 |
≤1.0 |
≤2.0 |
17.0~19.0 |
8.0~11.0 |
- |
- |
5*(c%-0.02~0.8 |
≤0.03 |
≤0.035 |
- |
321H |
SUS312H |
X12CrNi -Ti18.9 |
2Cr13 |
0.16~0.25 |
≤1.0 |
≤1.0 |
12.0~14.0 |
≤0.6 |
- |
- |
|
≤0.03 |
≤0.035 |
- |
420 |
SUS420J1 |
X20Cr13 |
9Cr18MoV |
0.85~0.95 |
≤0.8 |
≤0.8 |
17.0~19.0 |
≤0.6 |
1.0~1.3 |
- |
|
≤0.03 |
≤0.035 |
- |
440B |
SUS440B |
X90CrMo -V18 |
0Cr17Ni7Al |
≤0.09 |
≤1.0 |
≤1.0 |
16.0~18.0 |
6.5~7.75 |
- |
≤0.5 |
|
≤0.03 |
≤0.035 |
0.75~1.5 |
17-7PH (631) |
SUS631 |
X7CrNi -A117.7 |
1Cr18Ni9 |
≤0.15 |
≤1.0 |
≤2.0 |
17.0~19.0 |
8.0~10.0 |
- |
- |
- |
≤0.03 |
≤0.035 |
- |
302 |
SUS302 |
|
Y1Cr18Ni9 |
≤0.15 |
≤1.0 |
≤2.0 |
17.0~19.0 |
8.0~10.0 |
需要时加≤0.6 |
- |
|
≤0.15 |
≤0.20 |
- |
303 |
SUS303 |
X12CrNi -S18.8 |
0Cr18Ni9 |
≤0.07 |
≤1.0 |
≤2.0 |
17.0~19.0 |
8.0~11.0 |
|
- |
|
≤0.03 |
≤0.035 |
- |
304 |
SUS304 |
X5Cr- Ni18.9 | |
产品名称标准 |
牌号 |
化学成分% |
国外产品牌号 |
C |
Si |
Mn |
Cr |
Ni |
Mo |
Cu |
Ti |
S |
P |
N |
美国 |
日本 |
德国 |
不锈耐酸铸钢GB2100 -80 |
ZG1Cr18 Ni9Ti |
≤0.12 |
≤1.5 |
0.8~2.0 |
17.0~20.0 |
8.0~11.0 |
- |
- |
5X( C0.02) -0.7 |
0.03 |
0.045 |
- |
|
JIS:SCS22 |
|
ZG1Cr18N i12Mo2Ti |
≥0.12 |
≤1.5 |
0.8~2.0 |
16.0~19.0 |
11.0~13.0 |
2.0~3.0 |
- |
5X(C-0.02) 0/7 |
0.03 |
0.045 |
- |
|
JIS:SCS22 |
DIN:X6 CrNiMo -Nb1810W- Nr.1.4581 |
ZG00Cr 18Ni10 |
≤0.03 |
≤1.5 |
0.8~2.0 |
17.0~20.0 |
8.0~120 |
- |
- |
- |
0.03 |
0.04 |
- |
ACI:CF -3 USA: J92500 |
JIS:SCS19 |
DIN:G-X 2CrNi-189 |
ZG0Cr17Ni 14Cu4Nb |
≤0.07 |
≤1.0 |
≤1.0 |
15.5~17.5 |
3.0~5.0 |
- |
2.6~4.6 |
- |
≤0.03 |
≤0.035 |
- |
|
|
|
ZG1Cr18 Mn8Ni14N |
≤0.1 |
≤1.5 |
7.5~10.0 |
17.0~19.0 |
3.50~5.50 |
- |
- |
- |
≤0.03 |
≤0.06 |
0.12~0.25 |
|
|
|
ZG1Cr24Ni 20Mo2Cu3 |
≤0.12 |
≤1.5 |
0.8~2.0 |
23.0~25.0 |
19.0~21.0 |
2.0~3.0 |
3.0~4.0 |
- |
0.03 |
0.045 |
- |
|
|
|
ZG1Cr17Mn9 Ni14Mo3Gu2N |
≤0.12 |
≤1.5 |
8.0~10.0 |
16.0~19.0 |
3.0~5.0 |
2.9~3.5 |
2.0~2.5 |
- |
0.035 |
0.06 |
0.16~0.26 |
|
|
|
ZG1Cr18Mn 13Mo2GuN |
≤0.12 |
≤1.5 |
12.0~14.0 |
17.0~20.0 |
- |
1.5~2.0 |
1.5~2.0 |
|
0.035 |
0.06 |
0.19~2.6 |
|
|
|
ZG2Cr13 |
0.16~0.24 |
≤1.0 |
≤0.6 |
12.0~14.0 |
≤0.6 |
- |
- |
- |
≤0.03 |
≤0.04 |
- |
|
|
|
ZG1Cr13 |
0.08~0.15 |
≤1.0 |
≤0.6 |
12.0~14.0 |
- |
- |
- |
- |
0.03 |
0.04 |
- |
ACI:CA -15UNS:J91150 |
JIS:SCS1 |
DIN:G- X7Cr13 G-X10Cr13 |
ZG0Cr18Ni9 |
≤0.08 |
≤1.5 |
0.8~2.0 |
17.0~20.0 |
8.0~11.0 |
- |
- |
- |
0.03 |
0.04 |
- |
ACI:CF -8UNS:J92600 |
JIS:SCS13 |
DIN:G- X6CrNi189 |
ZG1Cr18Ni9 |
≤0.12 |
≤1.5 |
0.8~2.0 |
17.0~20.0 |
8.0~11.0 |
- |
- |
- |
0.03 |
0.045 |
- |
|
JIS:SCS12 SCS13A |
G-X10 CrNi188 |
ZGOCr18Ni9Ti |
≤0.08 |
≤1.5 |
0.8~2.0 |
17.0~20.0 |
8.0~11.0 |
- |
- |
5X(C -0.02) -0.7 |
0.03 |
0.04 |
- |
ACI:CF -8CUNS:J92710 |
SCS21 |
G-X5CrNi -Nb189 |
ZG0Cr18Ni -12Mo2Ti |
≤0.08 |
≤1.5 |
0.8~2.0 |
16.0~19.0 |
11.0~13.0 |
2.0~3.0 |
- |
5X(C-0.02) -0.7 |
0.03 |
0.04 |
- |
ACI:CF -8MUNS:J92900 |
|
|
一般工程 用铸钢GB5676 -85 |
ZG200-400 |
C |
Mn |
Si |
S |
P |
残余元素 |
U-60-30 |
SC410 |
|
Ni |
Cr |
Cu |
Mo |
V |
0.2 |
0.8 |
0.5 |
0.04 |
0.04 |
0.3 |
0.35 |
0.3 |
0.2 |
0.05 |
ZG230-450 |
0.3 |
0.9 |
0.5 |
0.04 |
0.04 |
0.3 |
0.35 |
0.3 |
0.2 |
0.05 |
65-35 |
450 |
|
ZG270-500 |
0.4 |
0.9 |
0.5 |
0.04 |
0.04 |
0.3 |
0.35 |
0.3 |
0.2 |
0.05 |
|
|
|
ZG310-570 |
0.5 |
0.9 |
0.6 |
0.04 |
0.04 |
0.3 |
0.35 |
0.3 |
0.2 |
0.05 |
80-40 |
|
| |
产品名 称标准 |
牌号 |
化学成分% |
国外产品牌号 |
C |
Si |
Mn |
Cr |
Ni |
Mo |
Cu |
Ti |
S |
P |
N |
美国 |
日本 |
德国 |
普通碳素 结构钢 GB700-88 |
Q215 (A2、C2) |
0.09~0.15 |
≤0.3 |
0.25~0.55 |
- |
- |
- |
- |
- |
≤0.05 |
≤0.045 |
- |
1010 |
SBC300 |
C15 |
Q235 (A3、C3) |
0.14~0.22 |
≤0.3 |
0.3~0.65 |
- |
- |
- |
- |
- |
≤0.05 |
≤0.045 |
- |
1015 |
SCD3 |
C22 |
Q255 (A4、C4) |
0.18~0.28 |
≤0.3 |
0.4~0.7 |
- |
- |
- |
- |
- |
≤0.05 |
≤0.045 |
- |
1020 1023 1025 |
SCD4 |
C22 |
优质碳素 结构钢 GB699-88 |
10 |
0.07~0.14 |
0.17~0.37 |
0.35~0.65 |
≤0.15 |
≤0.25 |
- |
≤0.25 |
- |
≤0.035 |
≤0.035 |
- |
1010 1012 |
SWRCH10A |
CK10 |
15 |
0.12~0.17 |
0.17~0.37 |
0.35~0.65 |
≤0.25 |
≤0.25 |
- |
≤0.25 |
- |
≤0.035 |
≤0.035 |
- |
1015 1017 |
SWRCH15A |
CK15 |
25 |
0.22~0.30 |
0.17~0.37 |
0.5~0.8 |
≤0.25 |
≤0.25 |
- |
≤0.25 |
- |
≤0.035 |
≤0.035 |
- |
1025 1026 1029 |
SWRCH25K |
CK25 |
30 |
0.27~0.35 |
0.17~0.37 |
0.5~0.8 |
≤0.25 |
≤0.25 |
- |
≤0.25 |
- |
≤0.035 |
≤0.035 |
- |
1030 1034 |
SWRCH30K |
CK30 |
35 |
0.32~0.40 |
0.17~0.37 |
0.5~0.8 |
≤0.25 |
≤0.25 |
- |
≤0.25 |
- |
≤0.035 |
≤0.035 |
- |
1034 1035 |
SWRCH35K |
CK35 |
45 |
0.42~0.50 |
0.17~0.37 |
0.5~0.8 |
≤0.25 |
≤0.25 |
- |
≤0.25 |
- |
≤0.035 |
≤0.035 |
- |
1045 |
SWRCH45K |
CK45 |
|
C |
Si |
Mn |
Cr |
Ni |
Mo |
Cu |
Ti |
S |
P |
V |
|
|
|
弹簧钢 GB1222-84 |
55SiMn |
0.52~0.60 |
1.5~2.0 |
0.6~0.9 |
≤0.35 |
≤0.35 |
- |
≤0.25 |
- |
≤0.035 |
≤0.035 |
- |
9255 |
SUP6 SUP7 |
55Si7 |
60Si2Mn |
0.56~0.64 |
1.5~20.0 |
0.6~0.9 |
≤0.35 |
≤0.35 |
- |
≤0.25 |
- |
≤0.035 |
≤0.035 |
- |
9260 |
SUP6 SUP7 |
60SiMn5 |
60Si2MnA |
0.56~0.64 |
1.6~2.0 |
0.6~0.9 |
≤0.35 |
≤0.35 |
- |
≤0.25 |
- |
≤0.03 |
≤0.03 |
- |
|
|
|
碳素工具钢 GB1298-86 |
T8、T8A |
0.75~0.84 |
≤0.35 |
≤0.4 |
≤0.25 |
≤0.2 |
- |
≤0.3 |
- |
≤0.03 |
≤0.03 |
- |
W1-8 |
SK5 |
C85W |
T9、T9A |
0.85~0.94 |
≤0.35 |
≤0.4 |
- |
- |
- |
- |
- |
≤0.03 |
≤0.03 |
- |
W1-8.5 |
SK4 |
|
T10、T10A |
0.95~1.04 |
≤0.35 |
≤0.4 |
- |
- |
|
- |
|
≤0.03 |
≤0.03 |
- |
W1-9.5 |
SK3 |
C105W2 | |