1.
The iron- ore slag of different contents was added to SiC kiln furniture bonded with fine silicon powder.
在硅微粉结合的SiC窑具材料中添加不同含量的铁矿渣,铁矿渣中的Fe2O3在高温下形成一定数量的液相,能使硅微粉析出的α—方石英转变为稳定的α—磷石英,提高窑具材料的热稳定性和强度,延长使用寿命。
2.
Adding fused MnO2-CaF2 Mineralizer into fine silicon powder can change its cryst al structure and improve the amount of tridymite,thus can improve the kiln furni ture's high temperature properties and prolong its lifetime.
MnO2-CaF2混合矿化剂能改善硅微粉析晶结构,增加磷石英的含量,从而改善窑具的高温性能,延长使用寿命;采用XRD法测定析晶结构,并测定窑具的抗折强度、抗折强度保持率、气孔率、吸水率等各项性能指标,综合分析得出MnO2-CaF2混合矿化剂的最佳加入量为2%。
3.
Add CaO-MnO 2 mineralizer to the SiC kiln furniture bonded with fine silicon powder can reduce the oxidation degree dramatically.
在硅微粉结合的SiC窑具中添加CaO -MnO2 混合矿化剂可显著降低SiC窑具的氧化度。
5) Microsilica
硅微粉
1.
The effect of microsilica on the flowability of matrix slurry was studied by using various type of microsilica.
采用不同硅微粉,研究了其对高铝浇注料基质泥浆粘度的影响,结果表明,基质泥浆粘度随硅微粉加入量增加而增大。